PETG Transparent
SUNLU PETG Transparent delivers high transparency with improved strength and toughness compared to PLA.
Diameter：
Weight：
Transparent and vibrant, with excellent yellowing resistance
This material has exceptional transparency, with printed models having a glossy and vibrant finish, clearly showing every detail. Its excellent yellowing resistance ensures that, after prolonged use, the model surface remains bright and like new, avoiding yellowing issues and maintaining a clear, transparent appearance over time.
Good toughness, less prone to breakage during printing
The material offers excellent toughness, allowing printed models to withstand significant external impacts, preventing breakage during use. Even in high-stress environments, the printed parts maintain outstanding durability and reliability.
1.75 ± 0.02 mm diameter tolerance, high printer compatibility
With precise diameter control and a tolerance of just ±0.02mm, this filament ensures stability and accuracy during every print. Its strong device compatibility means it works seamlessly with most FDM printers on the market, guaranteeing stable and precise print results.
Neat filament winding reduces tangling and nozzle clogging risk
The optimized winding design ensures that the filament is neatly wound, significantly reducing the risk of tangling and clogging. Each print proceeds smoothly, minimizing disruptions during operation and improving print stability and success rates.
Parameter Information
| Mechanical Properties | Physical Properties | Print Settings | |||
|---|---|---|---|---|---|
| Tensile Strength（MPa） | 48±10 | Density（g/cm³） | 1.27 | Nozzle Temperature & Print Speed | 240-260℃ / ≤300mm/s |
| Flexural Strength（MPa） | 70±10 | Melt Flow Index（g/10 min） | 5.7±3 | Bed Temperature | 60-70℃ |
| Notched Izod Impact Strength（KJ/m²） | 3±1 | Shrinkage（%） | 0.1-0.5 | Retraction Distance | 0.8-1.2mm |
| Elongation at Break（%） | 11±5 | Heat Deflection Temperature（℃） | 70±5 | Retraction Speed | 30-40mm/s |
| Shore Hardness（HA/HD） | 80 | Vicat Softening Temperature（℃） | / | ||