Flexible Resin
SUNLU Flexible Resin features Shore hardness 70A, with excellent tear resistance and tensile strength. Printed parts are flexible and durable, ideal for functional models requiring elasticity.
Weight：
70A Hardness with Silicone-Like Feel
The printed product has a silicone-like texture, with a soft feel and exceptional comfort. It is ideal for applications that require a soft and comfortable tactile experience, providing users with a superior touch experience.
Excellent Tear & Impact Resistance
The model features outstanding tear and impact resistance, able to withstand significant stretching and impact forces. This greatly enhances durability, making it resistant to damage even under harsh conditions.
High Elasticity & Rebound
With excellent stretchability and rebound ability, it can quickly return to its original shape, making it especially suitable for flexible applications such as seals, gaskets, and more. It offers high adaptability to shape deformation and external impacts.
Mixable to Adjust Hardness
This material can be mixed with other resins to adjust its hardness flexibly as a toughening agent. Whether it's increasing toughness, improving impact resistance, or adjusting hardness according to specific requirements, it offers highly customizable solutions to meet diverse application scenarios. This flexibility allows users to adjust the material properties as needed, ensuring outstanding performance of printed parts in various applications.
Parameter Information
| Mechanical Properties | Physical Properties | Print Settings | |||
|---|---|---|---|---|---|
| Tensile Strength（MPa） | 4 | Resin viscosity（mPa.s/℃） | ≤2000 | Bottom number | 5-10 |
| Flexural Strength（MPa） | / | Mold Shrinkage（%） | 7.38 | Bottom exposure time | Color LCD: 30-120s Monochrome LCD: 25–100s |
| Notched Izod Impact Strength（J/m） | / | Heat Deflection Temperature（℃） | / | Layer exposure time | Color LCD: 8–30s Monochrome LCD: 5–10s |
| Elongation at Break（%） | 130 | Lifting speed | 60-90mm/min | ||
| Shore Hardness（HA/HD） | 70 | ||||