High Speed PLA+2.0
SUNLU High Speed PLA+ 2.0 further improves toughness and strength, ensuring flat surfaces and reliable mechanical performance during high-speed printing.
Diameter：
Weight：
Supports printing speeds up to 600 mm/s, greatly improving efficiency
This material supports high-speed printing up to 600mm/s, significantly enhancing printing efficiency and reducing formation time. Whether for rapid prototyping or batch production, it can efficiently complete tasks, greatly improving overall work efficiency.
Toughness 2 to 3x higher than standard PLA, making prints less prone to damage
Compared to regular PLA materials, the toughness is increased by 2–3 times, offering superior impact resistance. The printed parts are more robust and durable, less prone to cracking or damage, meeting the needs of functional and structural applications.
Neat filament winding, reducing tangling and clogging risk
Using a precision winding process, the filament is tightly and orderly coiled, effectively reducing tangling, knotting, and clogging risks. This ensures a continuous and stable printing process, reducing interruptions and print failures.
1.75 ± 0.02 mm diameter tolerance, high printer compatibility
The filament diameter tolerance is strictly controlled, ensuring smooth and stable extrusion. This improves print accuracy and surface quality, while also enhancing device compatibility and print consistency.
Parameter Information
| Mechanical Properties | Physical Properties | Print Settings | |||
|---|---|---|---|---|---|
| Tensile Strength（MPa） | 40±3 | Density（g/cm³） | 1.27 | Nozzle Temperature & Print Speed | 200-215℃/50-150mm/s 215-230℃/150-300mm/s |
| Flexural Strength（MPa） | 73±5 | Melt Flow Index（g/10 min） | 10.2±3 | Bed Temperature | 50-60℃ |
| Notched Izod Impact Strength（kJ/m²） | 4.5±1.5 | Shrinkage（%） | / | Retraction Distance | 0.8-1.2mm |
| Elongation at Break（%） | 14±4 | Heat Deflection Temperature（℃） | 56.5±3 | Retraction Speed | 30-40mm/s |
| Shore Hardness（HA/HD） | 86.5 | Vicat Softening Temperature（℃） | / | ||