Water-Wash ABS-Like Resin
SUNLU Water Wash ABS Resin offers the toughness and strength of ABS-like materials with the convenience of water-based cleaning, making post-processing easier for functional and structural prints.
Weight：
Smooth Flow, Easy to Print
The material offers outstanding hydrophilic properties, allowing the model to be directly cleaned with water after printing, without the need for additional solvents. The process is simple and efficient, enhancing convenience and being more environmentally friendly and safe, making it suitable for various printing scenarios.
Low Odor, Stable Performance
The material combines excellent impact resistance and bend resistance, effectively reducing the risk of damage during use or assembly. The finished product is more durable and stable, making it suitable for applications that require strength.
Excellent Hydrophilicity for Easy Water Cleaning
The flowability has been optimized to ensure smooth and even extrusion, effectively reducing issues like stringing and layer gaps. The printing process is more stable and seamless, improving molding accuracy and success rates, providing users with a more effortless and worry-free printing experience.
Low Odor, Stable Performance
Using a low-odor optimized formula, this material effectively reduces irritating smells during the printing process, enhancing user comfort. Its performance remains stable and reliable, ensuring excellent results even during long print sessions.
Parameter Information
| Mechanical Properties | Physical Properties | Print Settings | |||
|---|---|---|---|---|---|
| Tensile Strength（MPa） | 26 | Resin viscosity（mPa.s/℃） | 400-800 | Bottom number | 5-10 |
| Flexural Strength（MPa） | 34 | Mold Shrinkage（%） | 8.8 | Bottom exposure time | Color LCD: 20-80s Monochrome LCD: 10–60s |
| Notched Izod Impact Strength（J/m） | 120 | Heat Deflection Temperature（℃） | 47 | Layer exposure time | Color LCD: 4–15s Monochrome LCD: 2–4s |
| Elongation at Break（%） | 24 | Lifting speed | 60-120mm/min | ||
| Shore Hardness（HA/HD） | 77 | ||||